Phosphor blend for an led light source and led light source incorporating same

ABSTRACT

A phosphor blend for an LED light source is provided wherein the phosphor blend comprises from about 7 to about 12 weight percent of a cerium-activated yttrium aluminum garnet phosphor, from about 3 to about 6 weight percent of a europium-activated strontium calcium silicon nitride phosphor, from about 15 to about 20 weight percent of a europium-activated calcium silicon nitride phosphor, and from about 55 to about 80 weight percent of a europium-activated calcium magnesium chlorosilicate phosphor. An LED light source in accordance with this invention has a B:G:R ratio for a 3200 K tungsten balanced color film of X:Y:Z when directly exposed through a nominal photographic lens, wherein X, Y and Z each have a value from 0.90 to 1.10.

CROSS REFERENCES TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No. 61/234,518, filed Aug. 17, 2009.

TECHNICAL FIELD

This invention relates to lighting for photography and cinematography, especially to the use of light emitting diodes (LEDs) for these applications.

BACKGROUND OF THE INVENTION

Lighting for the film industry started with sunlight about the beginning of the last century and thereafter evolved through the carbon arc to a mix of incandescent lamps, medium arc high intensity discharge lamps (e.g., HMI), and more recently, fluorescent lighting. To a greater or lesser extent, these light sources all required large amounts of electric power and generate large amounts of heat that is undesirable during film production. High power consumption is an especially difficult problem for location production where a supply of electric power may be limited unless portable electric generating plants are made available which can increase the cost of production.

In addition, the films that have been developed over the years have been standardized to a degree to have responses based on the spectral characteristics of specific light sources. In particular, two widely used films have based their responses on a incandescent 3200K tungsten source and a standard 5500 K daylight source as exemplified by KODAK Color Negative Film 5219 and KODAK Color Negative Film 5205, respectively. It is important therefore that any new light sources which might be developed for photography or cinematography have appropriate spectral power distributions for use with these films.

SUMMARY OF THE INVENTION

It is an object of the invention to obviate the disadvantages of the prior art.

It is a another object of the invention to provide a light source based on LEDs with the major objectives of reducing heat in the vicinity of the light sources and, more importantly, reducing the power required to operate such lighting.

It is a further object of the invention to provide a light source having a spectral power distribution appropriate for a 3200 K tungsten film.

In accordance with an aspect of the invention, there is provided a phosphor blend for an LED light source comprising from about 7 to about 12 weight percent of a cerium-activated yttrium aluminum garnet phosphor, from about 3 to about 6 weight percent of a europium-activated strontium calcium silicon nitride phosphor, from about 15 to about 20 weight percent of a europium-activated calcium silicon nitride phosphor, and from about 55 to about 80 weight percent of a europium-activated calcium magnesium chlorosilicate phosphor.

Preferably, the phosphor blend comprises from about 8 to about 10.5 weight percent of the cerium-activated yttrium aluminum garnet phosphor, from about 4 to about 5 weight percent of the europium-activated strontium calcium silicon nitride phosphor, from about 16.5 to about 18.5 weight percent of the europium-activated calcium silicon nitride phosphor, and from about 65 to about 75 weight percent of the europium-activated calcium magnesium chlorosilicate phosphor.

More preferably. the phosphor blend of comprises about 10 weight percent of the cerium-activated yttrium aluminum garnet phosphor, about 4.5 weight percent of the europium-activated strontium calcium silicon nitride phosphor, about 17.5 weight percent of the europium-activated calcium silicon nitride phosphor, and about 68 weight percent of the europium-activated calcium magnesium chlorosilicate phosphor.

In accordance with another aspect of the invention, there is provided an LED light source having a B:G:R ratio for a 3200 K tungsten balanced color film of X:Y:Z when directly exposed through a nominal photographic lens, wherein X, Y and Z each have a value from 0.90 to 1.10.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates the three film response sensitivities for 3200 K tungsten film.

FIG. 2 shows the relative spectral power distribution of a 3200 K incandescent light source.

FIG. 3 shows the average lens spectral transmittance used in the standard ANSI PH2.3-1972.

FIG. 4 shows a spectrum of an embodiment of an LED light source according to this invention for use with 3200 K tungsten balanced color film.

FIG. 5 shows the chromaticity point of the LED light source on the 1931 CIE Chromaticity Diagram.

FIG. 6 shows the individual emission curves for the four phosphors comprising the phosphor blend according to this invention.

FIG. 7 is a top view of an array of LED light sources according to this invention.

FIG. 8 is a cross-sectional illustration of one of the LED light sources shown in FIG. 7.

DETAILED DESCRIPTION OF THE INVENTION

In a preferred embodiment, the LED light source comprises either discrete LED elements or arrays of nominally identical elements that can be arranged in various ways to form a complete light source. The color quality as described by the spectral power distribution is balanced to satisfy the exposure requirements of 3200 K tungsten film as exemplified by KODAK Color Negative Film 5219 although the LED source generally will function satisfactorily with other films nominally balanced for 3200 K tungsten. The sine qua non is that non-selectively reflecting surfaces will be reproduced achromatically by the developed film. It will be noted that trichromatic films of this type cannot ever reproduce all possible colored reflective surfaces identically to their direct visual appearances irrespective of the light source spectral power distribution that is used. This well-known limitation is described in Kodak Publication No. E-73, Why a Color May Not Reproduce Correctly (312-10-78-DX, 1978).

3200 K tungsten film is nominally balanced to give proper color reproduction with an incandescent lamp radiating at a color temperature (CIE 15:2004) of 3200 K. However, certain spectral power distributions that differ from this one can be made acceptable. Note that an acceptable alternative does not necessarily have to have a correlated color temperature (CIE 15:2004) of 3200 K. Regardless of the actual correlated color temperature of the LED source, it is identified as a 3200 K photographic light indicating that it is to be used with 3200 K tungsten balanced film. Further, it is well-known that handheld photographic color temperature meters may not indicate either 3200 K or the actual correlated color temperature of the LED source. The light does not have to have any particular visual appearance in terms of color quality, and it does not have to meet any particular color quality metric for visual purposes. Parenthetically, we will note that the General Color Rendering Index (CIE 13.3-1995) of an acceptable light for this application commonly will fall in an acceptable range of values for commercial lighting lamps, i.e., roughly 70 or higher. The basic requirement is that the photographic system reproduces color in a proper and acceptable manner.

The method for designing the light source is to control three metric values proportional to the three components of the film response when the film is directly exposed to the light source spectrum. The three components are called the blue (B), green (G), and red (R) responses because the three film component sensitivities fall in the regions of the spectrum that are so described. FIG. 1 illustrates the three film response sensitivities. We observe that the blue component is most sensitive, the red component is least sensitive, and the green component is intermediate.

FIG. 2 shows the relative spectral power distribution of a 3200 K incandescent (i.e., tungsten) light source. When this spectral power is independently weighted by each of the three spectral sensitivities, the resulting blue (B), green (G), and red (R) responses are proportional to the areas under the respective product curves. The necessary condition for the required achromatic reproduction of a non-selectively reflecting surface is that B:G:R is in the proportions of 1:1:1. This establishes the “white point” for the film exposure. We note that the spectral power of the 3200 K incandescent source increases monotonically from lower to higher wavelengths, a variation that is in opposition to that of the areas under the three sensitivity curves versus wavelength. Clearly the balance of film sensitivities has been set to give three equal responses under a 3200 K incandescent light source.

As an essential component of the computation for the desired light source spectral distribution, note that the blue sensitivity of the film extends below 400 nm into the ultraviolet region of the spectrum. If the design were to proceed with the inherent blue film sensitivity, nonvisible radiation would influence the white point balance. But we also note that photographic lenses attenuate short wavelength radiation to a greater or lesser extent in the ultraviolet and sometimes well into the violet and blue regions of the visible spectrum. The effect depends on the various glasses used in manufacturing of a particular photographic camera lens and on the various lens coatings commonly used to reduce surface reflections at the various glass surfaces within the lens. The best we can do when designing a photographic light source to be used with a particular film is to make an average correction that is reasonably representative for most lenses. In this instance, we select the average lens spectral transmittance that is used in the standard ANSI PH2.3-1972. This lens transmittance (see FIG. 3) greatly reduces the blue response of the film to UV in a light source. The product of the blue film sensitivity and the typical average lens transmittance results in an effective blue film response as shown by the dashed line in FIG. 1. It is this modified blue response that is used in the LED design process. If the lens transmittance did not attenuate in the visible spectrum, this would be a moot point for an LED system in which the LED system does not radiate in the ultraviolet. However, the attenuation in the blue end of the visible spectrum above 400 nm will affect the white point balance.

The final acceptance of an LED or most other types of light sources for photography and cinematography cannot be set by computational or measurement means. It anticipated and expected that each light will have minor and subtle effects on the film exposure. These only can be determined by film tests using the actual or typical scenes. The lighting director will look at the resulting photography and make a decision of acceptability. If it is not quite to his liking, a weak color compensating and/or light balancing filter will be placed in front of the light. At the same time another lighting director may prefer the light without the filter(s) rather than the light changed by the filter. Because this is an issue of human preference, we do not expect universal agreement on the exact characteristics of a preferred light. Other issues such as the variation of any particular lens from the average typical lens transmittance will have a small effect on the performance of the light interacting with the film response. Many other minor factors are known and controlled to a greater or lesser extent. Examples of such factors would be deviations in the particular batch of film stock, the developing process, nonlinearities in the photographic process, etc. Consequently, some small variation in the B:G:R ratio characterizing an acceptable light source is expected and will not be significant providing that it is not excessive. When making final evaluative judgments of the color balance, there may be small displacements in the target design ratio due to such factors as the blue cutoff of the actual lens used in the evaluation.

What we have invented is a phosphor blend and an LED light source designed for use in conjunction with color film balanced for 3200 K incandescent (tungsten) lighting. The ratio of the three color components of the film, B:G:R, when directly exposed through a nominal photographic lens, is 1:1:1. The acceptable variability for this invention is defined at ±20% for each of the three numerical values. Preferably, the LED light source has a B:G:R ratio for a 3200 K tungsten balanced color film of X:Y:Z when directly exposed through a nominal photographic lens, wherein X, Y and Z each have a value from 0.90 to 1.10.

FIG. 4 shows an exemplary LED light source according to an embodiment of this invention for use with 3200 K tungsten balanced color film. The B:G:R ratio is 1.00:1.09:0.99. While visible metrics are irrelevant for this invention in its intended application, such values may aid is visualizing this light source. The correlated color temperature is 3257 K while the general color rendering index is 95. In a preferred embodiment, the LED sources use blue-emitting LED chips with phosphor embedded domes that provide the full required spectral range. Blue-emitting LEDs with dominate wavelengths in the range of 455-465 nm are typically used and the phosphor embedded domes contain a four-component blend of phosphors.

The four phosphor components in the blend include (1) a europium-activated calcium magnesium chlorosilicate phosphor, preferably having a composition represented by the formula, Ca₈Mg(SiO₄)₄Cl₂:Eu²⁺, and having a peak emission at about 500-510 nm; (2) a europium-activated strontium calcium silicon nitride phosphor, preferably having a composition represented by the formula, Sr_(2-x)Ca_(x)Si₅N₈:Eu²⁺, and having a peak emission at about 655-665 nm; (3) a europium-activated calcium silicon nitride phosphor, preferably having a composition represented by the formula, Ca₂Si₅N₈:Eu²⁺, and having a peak emission at about 610-620 nm; and (4) a cerium-activated yttrium aluminum garnet phosphor, preferably having a composition represented by the formula, Y₃Al₅O₁₂:Ce³⁺, and having a peak emission at about 560-570 nm. The preferred phosphor blend in Table I was developed to couple with the spectral response of common tungsten balanced films. Depending on the geometry of the part containing the phosphor blend (dome volume converted package) the concentration of the phosphor blend in the silicone matrix will vary. Typical values are 5-10 weight percent (wt %) phosphor blend in the silicone matrix.

TABLE I Preferred composition of the 3200K tungsten phosphor blend. Phosphor dominant Phosphor Wt % wavelength (nm) Ca₈Mg(SiO₄)₄Cl₂: Eu²⁺ 68.2 524 Ca₂Si₅N₈: Eu²⁺ 17.5 594 Sr_(2−x)Ca_(x)Si₅N₈: Eu²⁺ 4.5 608 Y₃Al₅O₁₂: Ce³⁺ 9.8 573

FIG. 5 shows the chromaticity point of the LED light source on the 1931 CIE Chromaticity Diagram where correlated color temperature lines are labeled in kelvin. The chromaticity, the correlated color temperature, and the general color rendering index are not given tolerances because they are dependent variables; B, G, and R are the independent variables. FIG. 6 shows the individual emission curves for the four phosphors comprising the blend. The phosphors are excited by the blue light emission from the blue LED and the light emitted by the phosphors combines with the remaining blue emission from the LED to produce the desired spectral output.

FIG. 7 is a top view of an array of LED light sources according to this invention. The LED light sources 10 are mounted on a circuit board 20 in a 5×5 array. The circuit board 20 is fitted with an electrical connector 15 for supplying power to the LED light sources. A cross-sectional illustration of one of the LED light sources 10 is shown in FIG. 8. The LED die 25 is mounted to the circuit board 20 and is covered by a phosphor-filled dome 30. The dome contains the 4-component phosphor blend. The space 35 between the LED die 25 and the dome 30 is preferably filled with a transparent silicone resin.

While there have been shown and described what are at present considered to be preferred embodiments of the invention, it will be apparent to those skilled in the art that various changes and modifications can be made herein without departing from the scope of the invention as defined by the appended claims. 

1. A phosphor blend for an LED light source comprising from about 7 to about 12 weight percent of a cerium-activated yttrium aluminum garnet phosphor, from about 3 to about 6 weight percent of a europium-activated strontium calcium silicon nitride phosphor, from about 15 to about 20 weight percent of a europium-activated calcium silicon nitride phosphor, and from about 55 to about 80 weight percent of a europium-activated calcium magnesium chlorosilicate phosphor.
 2. The phosphor blend of claim 1 wherein the blend comprises from about 8 to about 10.5 weight percent of the cerium-activated yttrium aluminum garnet phosphor, from about 4 to about 5 weight percent of the europium-activated strontium calcium silicon nitride phosphor, from about 16.5 to about 18.5 weight percent of the europium-activated calcium silicon nitride phosphor, and from about 65 to about 75 weight percent of the europium-activated calcium magnesium chlorosilicate phosphor.
 3. The phosphor blend of claim 1 wherein the blend comprises about 10 weight percent of the cerium-activated yttrium aluminum garnet phosphor, about 4.5 weight percent of the europium-activated strontium calcium silicon nitride phosphor, about 17.5 weight percent of the europium-activated calcium silicon nitride phosphor, and about 68 weight percent of the europium-activated calcium magnesium chlorosilicate phosphor.
 4. The phosphor blend of claim 1 wherein the cerium-activated yttrium aluminum garnet phosphor has a composition represented by a formula Y₃Al₅O₁₂:Ce³⁺, the europium-activated strontium calcium silicon nitride phosphor has a composition represented by a formula Sr_(2-x)Ca_(x)Si₅N₈:Eu²⁺, the europium-activated calcium silicon nitride phosphor has a composition represented by a formula Ca₂Si₅N₈:Eu²⁺, and the europium-activated calcium magnesium chlorosilicate phosphor has a composition represented by a formula Ca₈Mg(SiO₄)₄Cl₂:Eu2+.
 5. An LED light source having a B:G:R ratio for a 3200 K tungsten balanced color film of X:Y:Z when directly exposed through a nominal photographic lens, wherein X, Y and Z each have a value from 0.90 to 1.10.
 6. An LED light source having a B:G:R ratio for a 3200 K tungsten balanced color film of 1.00:1.09:0.99 when directly exposed through a nominal photographic lens. 